| Inkcazo | Uluhlu okanye Iinketho |
| Ukutyeba | 0.2mm ukuya kwi-250mm |
| Ububanzi | 500 mm uya 2500 mm |
| Ubude | 1000 mm uya 12000 mm |
| Ukucaphuka | O, H111, H32, kunye nabanye (H12 ukuya H38) |
| Unyango loMphezulu | Ukusila, ukupholisha, ukubrasha, i-anodizing, njl. |
Iialloyi zeAluminiyam ziyaziwa ngokuguquguquka kwazo kunye namandla-to-weight ratio, ukwenza ukuba babe lukhetho oludumileyo kuwo wonke amashishini ahlukeneyo. Phakathi kwezi alloys, i 5454 Icwecwe leAluminiyam yePhepha ligqame ngamandla ayo aphezulu, ukumelana nomhlwa okugqwesileyo, kunye nokwakheka okuphezulu. Eli nqaku ligocagoca kwiinkcukacha ze 5454 Icwecwe leAluminiyam yePhepha, iingenelo zayo, iinkcukacha, iimpawu zoomatshini, izicelo, kunye nokuninzi.
I 5454 Icwecwe leAluminiyam yeAluminiyam yialluminiyam-i-magnesium ialloy ephezulu esetyenziswa kakhulu kulwakhiwo lweenqanawa kunye namashishini othutho.. Yaziwa ngokugqwesa kwayo ukumelana nomhlwa, ngakumbi kumanzi olwandle kunye nezinye iimeko ezingqongileyo ezinomhlwa, iyenza ilungele izicelo zaselwandle.
Ukwakhiwa kweekhemikhali ze 5454 ipleyiti ye-aluminium ibaluleke kakhulu kwiimpawu zayo zokusebenza. Nalu ucazululo oluneenkcukacha:
| Isiqalelo secandelo | Metric Percentage Range |
|---|---|
| Aluminiyam (Al) | 94.4 – 97.1 % |
| Chromium (Cr) | 0.05 – 0.20 % |
| Ubhedu (Cu) | ≤ 0.10 % |
| Intsimbi (Fe) | ≤ 0.40 % |
| Magnesium (Mg) | 2.4 – 3.0 % |
| IManganese (Mnu) | 0.50 – 1.0 % |
| Okunye, nganye | ≤ 0.05 % |
| Okunye, iyonke | ≤ 0.15 % |
| Isilicon (Kwaye) | ≤ 0.25 % |
| I-Titanium (Kwe) | ≤ 0.20 % |
| Zinc (Zn) | ≤ 0.25 % |
I 5454 ipleyiti ye-aluminium inikezela ngoluhlu lweenzuzo ezenza kube yinto ekhethwayo kwizicelo ezininzi:
I 5454 ipleyiti ye-aluminiyam yephepha iyafumaneka kwiingqimba ezahlukeneyo, ububanzi, kunye nobude, kwaye inokubonelelwa ngeendlela ezahlukeneyo:
| Inkcazo | Uluhlu okanye Iinketho |
| Ukutyeba | 0.2mm ukuya kwi-250mm |
| Ububanzi | 500 mm uya 2500 mm |
| Ubude | 1000 mm uya 12000 mm |
| Ukucaphuka | O, H111, H32, kunye nabanye (H12 ukuya H38) |
| Unyango loMphezulu | Ukusila, ukupholisha, ukubrasha, i-anodizing, njl. |
Ukuqonda iimpawu zoomatshini ze 5454 aluminiyam sheet plate is essential for determining its suitability for various applications, since the mechanical properties of 5454 alloys of different temperatures vary greatly, taking the O state as an example, the following table shows the mechanical properties of 5454-O:
| IPropati yoomatshini | Metric Value | Conditions/Comments |
|---|---|---|
| Ukuqina, Brinell | 62 | AA; Isiqhelo; 500 g load; 10 mm ibhola |
| Ukuqina, Knoop | 85 | Converted from Brinell Hardness Value |
| Ukuqina, Vickers | 72 | Converted from Brinell Hardness Value |
| Tensile strength, Eyokugqibela | 248 MPa | AA; Isiqhelo |
| 41.0 MPa | @ 371 °C / 700 °F | |
| 75.0 MPa | @ 316 °C / 601 °F | |
| 115 MPa | @ 260 °C / 500 °F | |
| 150 MPa | @ 204 °C / 399 °F | |
| 200 MPa | @ 149 °C / 300 °F | |
| 250 MPa | @ -28.0 °C / -18.4 °F | |
| 250 MPa | @ 24.0 °C / 75.2 °F | |
| 250 MPa | @ 100 °C / 212 °F | |
| 255 MPa | @ -80.0 °C / -112 °F | |
| 370 MPa | @ -196 °C / -321 °F | |
| Tensile strength, Yima kancinci | 117 MPa | AA; Isiqhelo |
| 29.0 MPa | @ 371 °C / 700 °F | |
| 50.0 MPa | @ 316 °C / 601 °F | |
| 75.0 MPa | @ 260 °C / 500 °F | |
| 105 MPa | @ 204 °C / 399 °F | |
| 110 MPa | @ 149 °C / 300 °F | |
| 115 MPa | @ -80.0 °C / -112 °F | |
| 115 MPa | @ -28.0 °C / -18.4 °F | |
| 115 MPa | @ 24.0 °C / 75.2 °F | |
| 115 MPa | @ 100 °C / 212 °F | |
| 130 MPa | @ -196 °C / -321 °F | |
| Ukwandiswa ngexesha lekhefu | 25 % | @ 24.0 °C / 75.2 °F |
| 27 % | @ -28.0 °C / -18.4 °F | |
| 30 % | @ -80.0 °C / -112 °F | |
| 31 % | @ 100 °C / 212 °F | |
| 39 % | @ -196 °C / -321 °F | |
| 50 % | @ 149 °C / 300 °F | |
| 60 % | @ 204 °C / 399 °F | |
| 80 % | @ 260 °C / 500 °F | |
| 110 % | @ 316 °C / 601 °F | |
| 130 % | @ 371 °C / 700 °F | |
| 22 % | @ Thickness 1.59 mm / 0.0625 kwi | |
| Imodyuli yeElasticity | 70.3 GPA | AA; Isiqhelo; Umyinge woxinzelelo kunye noxinzelelo. Compression modulus is about 2% greater than tensile modulus. |
| Notched Tensile Strength | 221 MPa | 2.5 cm width x 0.16 cm thick side-notched specimen, Kt = 17. |
| Ultimate Bearing Strength | 427 MPa | Edge distance/pin diameter = 2.0 |
| Bearing Yield Strength | 165 MPa | Edge distance/pin diameter = 2.0 |
| Ubungakanani bePisces | 0.33 | Estimated from trends in similar Al alloys. |
| Ukudinwa Amandla | 120 MPa | @ 5.00e+8 cycles; unnotched R. R. Moore rotating beam |
| Shear Modulus | 26.0 GPA | Estimated from similar Al alloys. |
| Shear Amandla | 159 MPa | AA; Isiqhelo |
This table provides a comprehensive overview of the mechanical properties of the 5454 ingxubevange, kuquka nobulukhuni, tensile strength, Ubude, modulus of elasticity, kunye nokuninzi, under various conditions and temperatures. I “Conditions/Comments” column provides additional details about the specific test parameters or the nature of the property measurement.
I 5454 Icwecwe lealuminiyam lifumana ukusetyenziswa kuluhlu olubanzi lwezicelo ngenxa yendibaniselwano eyodwa yeepropati:
I-5454-H32 ye-aluminiyam sheet plate isetyenziselwa iitanki zokugquma kunye neemoto zetanki ezikhazimlisiweyo, inika ukuqhelana nemekobume eyonakalisayo:
| Ipropati | Ixabiso |
| Tensile strength | 276 MPa |
| Unikeze Amandla | 207 MPa |
| Imodyuli yeElasticity | 70.3 GPA |
| Ukwandiswa ngexesha lekhefu | 18%
@Temperature 24.0 °C |
| Ukuqina | 73 Brinell |
I 5454 Ipleyiti ye-aluminiyam ye-H111 iphathwe ubushushu ukuze ibe namandla aphezulu kunye ne-ductility ephantsi, ezifanelekileyo kwizakhiwo zaselwandle kunye neenqanawa zoxinzelelo:
| Ipropati | Ixabiso |
| Tensile strength | 262 MPa |
| Unikeze Amandla | 179 MPa |
| Imodyuli yeElasticity | 70.3 GPA |
| Ukwandiswa ngexesha lekhefu | 14%
@Ukutyeba 1.59 mm |
| Ukuqina | 70 Brinell |
I 5454 O sheet aluminiyam ipleyiti, kwimo yokungena, inikeza i-ductility ephezulu kunye nokwakheka okulungileyo:
| Ipropati | Ixabiso |
| Tensile strength | 165 MPa |
| Unikeze Amandla | 65 MPa |
| Imodyuli yeElasticity | 70 GPA |
| Ukwandiswa ngexesha lekhefu | 25% |
| Ukuqina | 62 Brinell |
I 5454 I-aluminiyam yamkelwa ngemigangatho eyahlukeneyo, enokuthi inomahluko omncinci kwiinkqubo zokuvelisa okanye ukunyamezela:
Kubalulekile ukubonisana nomgangatho othile ofunekayo kwisicelo sakho ukuqinisekisa ukuba imathiriyeli iyahlangabezana neemfuno eziyimfuneko.
Ngemibuzo engaphezulu, iinkcukacha ezicacileyo, okanye ukufaka iodolo, uqhagamshelane Huasheng Aluminiyam, yakho ethembekileyo '5454 Aluminium Sheet Plate’ umzi-mveliso kunye nomthengisi. Iqela lethu leengcali likulungele ukukunceda ngazo zonke iimfuno zakho ze-aluminium.
Intshayelelo KwiHuawei Alumi.
Intshayelelo Kwi Huasheng Alu...
Wamkelekile kwiHuaSheng Aluminium……
KwiHuaSheng Aluminium, sithetha……
Wamkelekile kwiHuasheng Aluminium...
Wamkelekile kwiHuaSheng Aluminium……
UHenan Huasheng Aluminium Co., Ltd (HHALU ngokufutshane), isekwe kwi 2001, ibekwe kwidolophu yaseHuiguo, iAluminiyam eyinkunzi edumileyo yePhondo laseHenan, Ngumvelisi oqeqeshiweyo kwaye uzibandakanya kuphando, uphuhliso, imveliso, intengiso kunye nenkonzo aluminiyam sheet sheet, ikhoyili ye-aluminium, ifoyile yealuminiyam, aluminiyam strip kunye nesangqa aluminiyam.
Ukwengeza, I-HHALU iphinda ithengise ipleyiti ye-aluminium yokwakha kunye neenqanawa, ipleyiti yesipili yealuminiyam, kunye nepleyiti yealluminiyam yemoto.