Kupu Whakataki
Ko nga konumohe konumohe e mohiotia ana mo o raatau kaha me te kaha-ki-taimaha, ka waiho hei whiringa rongonui puta noa i nga momo ahumahi. I roto i enei koranu, te 5454 Ko te Pereti Rau Aluminium e tu ana mo tona kaha teitei, tino pai te aukati waikura, me te ahua pai ake. Ka rukuhia e tenei tuhinga nga korero motuhake o te 5454 Pereti Rau Aluminium, ona painga, whakaritenga, āhuatanga pūkaha, tono, me etahi atu.
He aha te 5454 Konumohe?
Ko te 5454 Ko te Pereti Rau Aluminium he konumohe-konupora teitei te kaha e whakamahia nuitia ana i roto i nga mahi hanga kaipuke me nga umanga kawe waka.. He rongonui mo tona tino pai te aukati i te waikura, otira ki te wai moana me etahi atu taiao pirau, kia pai mo nga tono moana.
Hangahanga matū
Te hanganga matū o 5454 He mea nui te pereti pepa konumohe mo ona ahuatanga mahi. Anei he wehewehenga taipitopito:
Huānga Waahanga |
Metric Percentage Range |
Konumohe (Ko Al) |
94.4 – 97.1 % |
Chromium (Cr) |
0.05 – 0.20 % |
Te parahi (Cu) |
≤ 0.10 % |
Te rino (Fe) |
≤ 0.40 % |
konupora (Mg) |
2.4 – 3.0 % |
konupora (Mn) |
0.50 – 1.0 % |
Ētahi atu, ia |
≤ 0.05 % |
Ētahi atu, katoa |
≤ 0.15 % |
Silicon (Na) |
≤ 0.25 % |
Titanium (O) |
≤ 0.20 % |
Zinc (Zn) |
≤ 0.25 % |
Painga o 5454 pereti pepa konumohe
Ko te 5454 Ko te pereti pepa konumohe he maha nga painga e pai ana mo nga tono maha:
- Te Kaha Rawa: Ka tuku i te tapatahi hanganga i roto i nga taiao kino.
- Tino Pai Atete Te Waikura: He pai mo te whakamahi i roto i te wai moana me nga taiao pirau.
- He pai te ahua: Ka taea te hanga ma te whakamahi i nga tikanga tikanga.
- Te paihere: He ngawari ki te hanga me te whakatika i nga tukanga.
- Mahinga miihini: Ka taea te mahi miihini me te whakaoti pai.
Whakatakotoranga o 5454 pereti pepa konumohe
Ko te 5454 Kei te waatea te pereti pepa konumohe i roto i nga momo matotoru, whanui, me te roa, a ka taea te tuku i roto i nga ahuatanga rereke:
Whakatakotoranga |
Awhe, Kōwhiringa ranei |
Mātotoru |
0.2mm ki te 250mm |
Whānui |
500 mm ki 2500 mm |
Te roa |
1000 mm ki 12000 mm |
Te riri |
O, H111, H32, me etahi atu (H12 ki H38) |
Maimoatanga Mata |
Te huri, whakakorikori, paraihe, anodizing, etc. |
Nga Taonga Miihini
Te maarama ki nga ahuatanga miihini o te 5454 He mea nui te pereti pepa konumohe mo te whakatau i tona pai mo nga momo tono, since the mechanical properties of 5454 alloys of different temperatures vary greatly, taking the O state as an example, the following table shows the mechanical properties of 5454-O:
Taonga Miihini |
Metric Value |
Conditions/Comments |
Te pakeke, Brinell |
62 |
AA; Tikanga; 500 g load; 10 mm pōro |
Te pakeke, Knoop |
85 |
Converted from Brinell Hardness Value |
Te pakeke, Vickers |
72 |
Converted from Brinell Hardness Value |
Te Kaha Toka, Mutunga |
248 MPa |
AA; Tikanga |
|
41.0 MPa |
@ 371 °C / 700 °F |
|
75.0 MPa |
@ 316 °C / 601 °F |
|
115 MPa |
@ 260 °C / 500 °F |
|
150 MPa |
@ 204 °C / 399 °F |
|
200 MPa |
@ 149 °C / 300 °F |
|
250 MPa |
@ -28.0 °C / -18.4 °F |
|
250 MPa |
@ 24.0 °C / 75.2 °F |
|
250 MPa |
@ 100 °C / 212 °F |
|
255 MPa |
@ -80.0 °C / -112 °F |
|
370 MPa |
@ -196 °C / -321 °F |
Te Kaha Toka, Tukunga |
117 MPa |
AA; Tikanga |
|
29.0 MPa |
@ 371 °C / 700 °F |
|
50.0 MPa |
@ 316 °C / 601 °F |
|
75.0 MPa |
@ 260 °C / 500 °F |
|
105 MPa |
@ 204 °C / 399 °F |
|
110 MPa |
@ 149 °C / 300 °F |
|
115 MPa |
@ -80.0 °C / -112 °F |
|
115 MPa |
@ -28.0 °C / -18.4 °F |
|
115 MPa |
@ 24.0 °C / 75.2 °F |
|
115 MPa |
@ 100 °C / 212 °F |
|
130 MPa |
@ -196 °C / -321 °F |
Elongation at Break |
25 % |
@ 24.0 °C / 75.2 °F |
|
27 % |
@ -28.0 °C / -18.4 °F |
|
30 % |
@ -80.0 °C / -112 °F |
|
31 % |
@ 100 °C / 212 °F |
|
39 % |
@ -196 °C / -321 °F |
|
50 % |
@ 149 °C / 300 °F |
|
60 % |
@ 204 °C / 399 °F |
|
80 % |
@ 260 °C / 500 °F |
|
110 % |
@ 316 °C / 601 °F |
|
130 % |
@ 371 °C / 700 °F |
|
22 % |
@ Thickness 1.59 mm / 0.0625 i roto |
Modulus of Elasticity |
70.3 GPa |
AA; Tikanga; Toharite o te mānukanuka me te kōpeketanga. Compression modulus is about 2% greater than tensile modulus. |
Notched Tensile Strength |
221 MPa |
2.5 cm width x 0.16 cm thick side-notched specimen, Kt = 17. |
Ultimate Bearing Strength |
427 MPa |
Edge distance/pin diameter = 2.0 |
Bearing Yield Strength |
165 MPa |
Edge distance/pin diameter = 2.0 |
Tauwehenga Pisces |
0.33 |
Estimated from trends in similar Al alloys. |
Te Kaha ngenge |
120 MPa |
@ 5.00e+8 cycles; unnotched R. R. Moore rotating beam |
Kōwae kutikuti |
26.0 GPa |
Estimated from similar Al alloys. |
Te Kaha Kutikuti |
159 MPa |
AA; Tikanga |
This table provides a comprehensive overview of the mechanical properties of the 5454 koranu, including hardness, kaha tensile, whakaroa, modulus of elasticity, me etahi atu, under various conditions and temperatures. Ko te “Conditions/Comments” column provides additional details about the specific test parameters or the nature of the property measurement.
Nga tono o 5454 pereti pepa konumohe
Ko te 5454 Ko te pereti pepa konumohe ka kitea te whakamahi i roto i te whānuitanga o nga tono na tona huinga ahurei o nga rawa:
- Nga tono moana: Te hanga poti, hanga kaipuke, me nga paipa moana.
- Te kawe waka: Nga taraka me nga tinana taraiwa, nga waahanga motuka.
- Nga Waka Peke: Nga taika me nga waka i roto i te umanga hinu me te hau.
- Hangahanga: Taika whakarara, nga waka taika kua orohia, me nga waahanga hanganga.
Tikanga 5454 Pereti Rau Aluminium
5454 H32 Pereti Rau Aluminium
Ko te pereti pepa konumohe 5454-H32 e whakamahia ana mo nga taika whakamaarama me nga waka taika orohia, te tuku urutau ki nga taiao pirau:
Taonga |
Uara |
Te Kaha Toka |
276 MPa |
Te Kaha Tuku |
207 MPa |
Modulus of Elasticity |
70.3 GPa |
Elongation at Break |
18%
@Temperature 24.0 °C |
Te pakeke |
73 Brinell |
5454 H111 Pereti Rau Aluminium
Ko te 5454 Ko te pereti pepa konumohe H111 he wera-wera mo te kaha ake me te iti o te ngawari, he pai mo nga hanganga moana me nga oko pehanga:
Taonga |
Uara |
Te Kaha Toka |
262 MPa |
Te Kaha Tuku |
179 MPa |
Modulus of Elasticity |
70.3 GPa |
Elongation at Break |
14%
@Matotoru 1.59 mm |
Te pakeke |
70 Brinell |
5454 E Pereti Rau Aluminium
Ko te 5454 E pereti pepa konumohe, i roto i te ahua annealed, tuku ductility tiketike, me te pai formability:
Taonga |
Uara |
Te Kaha Toka |
165 MPa |
Te Kaha Tuku |
65 MPa |
Modulus of Elasticity |
70 GPa |
Elongation at Break |
25% |
Te pakeke |
62 Brinell |
Nga Paerewa Taurite mo te Aluminium 5454
Ko te 5454 Ko te konumohe e mohiotia ana e nga momo paerewa, he iti nei nga rereketanga i roto i nga mahi whakangao, i nga whakangao ranei:
- US A95454
- ASTM B209
- AMS QQ-A-250/10
- EN AW-5454
- ISO AlMg3Mn