| Специфікація | Подробиці |
| сплав | 3003 Алюміній |
| Вдача | H24 |
| Товщина | 140мкм |
| Ширина | 100-1600 мм |
| Оздоблення поверхні | Coating Process |
As industries increasingly demand lightweight, стійкий до корозії, and highly formable materials, 140мкм 3003 H24 coated aluminum foil has become an important engineering material in packaging, будівництво, ізоляція, Системи ОВК, побутова техніка, і промислове виробництво.
Combining the excellent corrosion resistance of 3003 алюмінієвий сплав, the balanced mechanical properties of the Температура Н24, and the enhanced protection provided by specialized coating systems, this material offers an optimal combination of durability, технологічність, та економічна ефективність.
At a thickness of 140 мікрон (0.14 мм), the foil occupies a unique position between traditional aluminum foil and thin-gauge aluminum sheet.
It provides greater structural stability than ultra-thin foils while maintaining the flexibility and lightweight advantages associated with aluminum materials.
The combination of alloy composition, temper condition, and coating technology makes 140μm 3003 H24 coated aluminum foil an ideal material for applications requiring a balance between strength, стійкість до корозії, формувальність, and aesthetic appearance.
140мкм 3003 Алюмінієва фольга з покриттям H24
140мкм 3003 H24 coated aluminum foil is a precision-rolled aluminum product manufactured from AA3003 aluminum alloy, processed into the H24 temper condition, and subsequently coated with functional or decorative coatings to improve surface performance.
Thickness plays a critical role in determining the mechanical behavior and application suitability of aluminum foil.
Thickness Conversion
| одиниця | Значення |
|---|---|
| Micrometers | 140 мкм |
| Millimeters | 0.14 мм |
| Дюйми | 0.0055 в |
на 140 мікрон, the material is substantially thicker than conventional packaging foil, which typically ranges from 6–50 μm.
3003 алюмінієва фольга належить до Аль-Мн (Aluminum-Manganese) alloy family and is one of the most widely used aluminum alloys globally.
The alloy contains approximately 1.0–1.5% manganese, which significantly increases strength compared with commercially pure aluminum.
Typical Chemical Composition
| елемент | Зміст (%) |
|---|---|
| Алюміній (Ал) | Баланс |
| Марганець (Мн) | 1.0–1,5 |
| Мідь (Cu) | 0.05–0.20 |
| Кремній (І) | ≤0.60 |
| Залізо (Fe) | ≤0.70 |
| Цинк (Zn) | ≤0,10 |
Temper designation is critical in determining aluminum performance.
Definition of H24
According to aluminum temper classifications:
У практичному плані, 3003-H24 provides a balance between strength and ductility.
It is stronger and stiffer than annealed 3003-O, but more formable than harder tempers such as H26 or H18.
| Вдача | Strength Level | Формованість | Типове використання |
|---|---|---|---|
| 3003-О | Низький | Чудово | Deep drawing, soft forming |
| 3003-H14 | Середній | добре | General sheet and foil forming |
| 3003-H22 | Середньо-низький | Дуже добре | Moderate forming applications |
| 3003-H24 | Середньо-високий | добре | Фольга з покриттям, кришки, semi-rigid formed parts |
| 3003-H26 | Вища | Помірний | Stiffer parts with limited forming |
| 3003-H18 | Високий | Обмежений | High stiffness, minimal forming |
H24 is often selected when the foil must hold shape, resist deformation, and still tolerate forming or punching without cracking.
140мкм 3003 H24 Coated Aluminum Foil Packaged by Huasheng
The coating transforms the aluminum substrate into an application-specific material.
Depending on the end use, the coating may provide corrosion resistance, food-contact protection, heat-sealing performance, прикраса, ізоляція, or bonding compatibility.
| Тип покриття | Main Function | Типове застосування |
|---|---|---|
| Епоксидне покриття | Corrosion protection and adhesion | Lids, caps, industrial components |
| PE coating | Moisture resistance and heat sealing | Упаковка харчових продуктів, laminated foil |
| PP coating | Higher heat resistance than PE | Retort trays, hot-fill packaging |
| Polyester coating | Surface durability and decoration | Декоративні панелі, етикетки, ламінати |
| Термозварювальний лак | Controlled sealing performance | Молочні кришки, лотки, sealing membranes |
| Food-grade lacquer | Food-contact protection | Контейнери, кришки, meal trays |
| Пункт | Typical Specification / Reference Range |
|---|---|
| Назва продукту | 140мкм 3003 H24 coated aluminum foil |
| сплав | 3003 |
| Вдача | H24 |
| Товщина | 0.140 мм / 140мкм |
| Допуск по товщині | Commonly ±3–5%, or customer-specified |
| Ширина | Custom slit width, commonly 50–1600 mm |
| Внутрішній діаметер | 76 мм або 152 мм, customer-specified |
| Зовнішній діаметр | According to roll weight and packing requirement |
| Surface condition | чистий, з покриттям, flat, free from serious defects |
| Coating side | Single-side or double-side coating |
| Тип покриття | Епоксидна смола, поліестер, акрилові, PU, термозварювальний лак, hydrophilic, hydrophobic, ґрунтовка |
| Вага покриття | Often 1–10 g/m² per side, depending on coating function |
| Колір | Чіткий, золото, білий, кольоровий, or customer-specified |
| Лікування | Degreased, pretreated, з покриттям, cured |
| Упаковка | Wooden case or export seaworthy packing |
| Typical supply form | рулет, coil, лист, рельєфна фольга, coated stock |
For critical applications such as food-contact lids, pharmaceutical-related sealing foil, or HVAC fin stock, coating specifications should include adhesion, стійкість до корозії, sealing performance, and compliance declarations.
The performance of 140μm 3003 H24 coated aluminum foil is primarily determined by the mechanical characteristics of the 3003 alloy and the strengthening effect of the H24 temper.
| Власність | Типове значення |
|---|---|
| Міцність на розрив | 145–195 MPa |
| Межа текучості | ≥115 MPa |
| Подовження | 4–10% |
| Твердість (HV) | 45–60 |
| Модуль пружності | 69 ГПа |
| Власність | Значення |
|---|---|
| Щільність | 2.73 г/см³ |
| Теплопровідність | 180–210 W/m·K |
| Електропровідність | 40–45% IACS |
| Діапазон плавлення | 643–654°C |
| Thermal Expansion Coefficient | 23.6 × 10⁻⁶/K |
| Відбивна здатність | 80–88% |
140мкм 3003 H24 coated aluminum foil performs well when the application needs both strength and processability.
Main performance advantages include:
Coated Process of Aluminum Foil
Production begins with aluminum ingots and controlled alloying additions. Manganese gives 3003 its improved strength and corrosion resistance.
After casting and homogenization, the material passes through hot rolling and cold rolling to approach the target gauge.
The mill controls cold reduction and annealing to achieve H24 temper.
This step matters because excessive hardness may reduce formability, while insufficient hardness may cause poor shape retention.
Before coating, the foil surface needs proper cleaning and pretreatment.
Залишок масла, oxide instability, пил, or moisture can weaken coating adhesion.
The coating may be applied by roller coating, лакування, or lamination-related processes.
After application, controlled drying and curing create the required adhesion, гнучкість, і хімічна стійкість.
The coated foil is slit to the required width. Accurate slitting reduces burrs, edge cracks, and winding defects.
Stable tension control protects surface quality and prevents telescoping or coil deformation.
Inspection usually covers thickness, ширина, площинність, дефекти поверхні, coating adhesion, горілки, механічні властивості, and packaging quality.
140мкм 3003 H24 Coated Aluminum Foil for Construction
Універсальність 140мкм 3003 H24 coated aluminum foil stems from its balanced mechanical properties, відмінна стійкість до корозії, attractive surface finish, and ease of fabrication.
Its 140μm thickness provides greater rigidity than conventional foil while remaining lightweight and highly processable.
As a result, this material is widely used across construction, HVAC, упаковка, транспортування, appliance manufacturing, та промислові сектори.
The construction industry is one of the largest consumers of coated aluminum products.
Because aluminum possesses excellent thermal conductivity and reflectivity, 140мкм 3003 H24 coated foil is extensively used in HVAC applications.
Modern household appliances increasingly utilize coated aluminum components because of their durability and appearance.
Although thinner aluminum foils dominate flexible packaging, 140μm coated aluminum foil is frequently used in semi-rigid and specialty packaging applications.
Використана упаковка 3003 Алюмінієва фольга з покриттям
The transportation sector increasingly favors lightweight materials to improve energy efficiency.
Industrial manufacturers often require materials that combine durability with corrosion resistance.
The excellent surface quality of coated aluminum foil makes it suitable for visual applications.
The renewable energy sector has become an emerging market for coated aluminum materials.
| Власність | 3003 Алюмінієва фольга з покриттям H24 | 1050 Алюмінієва фольга | 5052 Алюмінієва фольга | Galvanized Steel | Нержавіюча сталь 304 |
|---|---|---|---|---|---|
| Щільність (г/см³) | 2.73 | 2.71 | 2.68 | 7.85 | 8.00 |
| Міцність на розрив (МПа) | 145–195 | 80–120 | 210–280 | 270–500 | 520–720 |
| Стійкість до корозії | Чудово | Чудово | Чудово | Помірний | Чудово |
| Формованість | Чудово | Чудово | добре | Помірний | Помірний |
| Теплопровідність (Вт/м·К) | 180–210 | 220–230 | 130–150 | 50 | 15 |
| вага | Дуже низький | Дуже низький | Дуже низький | Високий | Високий |
| Surface Coating Compatibility | Чудово | Чудово | Чудово | добре | Помірний |
| Вартість | Помірний | Низький | Вища | Низький | Високий |
Henan Huasheng Aluminium Co., ТОВ. is an aluminum supplier from Henan, Китай, offering aluminum sheet, плита, coil, смужка, and foil products for packaging and industrial applications.
For buyers of 140мкм 3003 H24 coated aluminum foil, supplier capability should focus on stable alloy control, coating reliability, export packaging, and technical communication.
Huasheng’s value for this product can be presented through practical buyer needs:
For best results, buyers should share the final application, forming depth, sealing temperature, coating requirement, and equipment width before ordering.
140мкм 3003 H24 coated aluminum foil is a practical, high-value material for packaging, container, кришка, laminate, і промислове застосування.
Його 0.14 товщина мм provides stronger puncture resistance and better shape retention than thin foil. 3003 Al-Mn alloy offers corrosion resistance and moderate strength.
Його Температура Н24 balances stability and formability. Нарешті, its coating system adds the exact function required by the final product, whether that means heat sealing, food-contact protection, прикраса, або стійкість до корозії.
Для виробників, the best purchasing decision depends on more than thickness and price. Тип покриття, адгезія, temper stability, якість поверхні, slitting accuracy, and supplier support all determine real production performance.
It is a 0.14 mm thick coated aluminum foil made from 3003 aluminum alloy in H24 temper. It is used for containers, кришки, лотки, ламінати, sealing membranes, and industrial coated foil products.
Так. 140μm = 0.14 мм, or about 5.51 млн.
3003 aluminum offers better strength than pure aluminum, хороша стійкість до корозії, and reliable formability. It suits packaging, контейнери, кришки, and coated foil applications.
H24 means the aluminum has been strain-hardened and partially annealed. It provides a useful balance of strength, гнучкість, and dimensional stability.
Так, if it uses a suitable food-grade coating and meets the required food-contact standards.
PE, пп, or heat-seal lacquer may work, depending on sealing temperature, food type, packaging structure, and equipment conditions.
Aluminum itself is recyclable, but coated foil recycling depends on coating type, contamination level, and local recycling systems. Clean industrial scrap usually has better recycling value.
1. вступ Як галузь……
вступ У світі……
8011 H18 блістер алюмінієвий для……
Вступ до 1050 Епоксид C……
1. вступ 8011 Тиснення……
1. Вступ до 3003 Галун……
Henan Huasheng Aluminium Co., ТОВ (HHALU скорочено), встановлено в 2001, знаходиться в місті Huiguo, знаменита алюмінієва столиця провінції Хенань, Це професійний виробник і займається дослідженнями, розвитку, виробництва, продажі та обслуговування алюміній листова пластина, алюмінієва котушка, алюмінієва фольга, алюмінієва стрічка та алюмінієвий круг.
В додаток, HHALU також продає алюмінієву пластину для будівництва та кораблів, алюмінієва дзеркальна пластина, і автомобільна пластина з алюмінієвого сплаву.
№53, Dongming Road, Чженчжоу, Хенань, Китай
Авторське право © Huasheng Aluminium 2025. Всі права захищені.