| Ukucaciswa | Ibanga noma Izinketho |
| Ubukhulu | 0.2mm kuya ku-250 mm |
| Ububanzi | 500 mm kwe 2500 mm |
| Ubude | 1000 mm kwe 12000 mm |
| Ulaka | O, H111, H32, nabanye (H12 kuya ku-H38) |
| Ukwelashwa Okungaphezulu | Ukugaya, ukupholisha, ukuxubha, i-anodizing, njll. |
Ama-alloys e-aluminium aziwa ngokuhlukahluka kwawo kanye nesilinganiso samandla nesisindo, okubenza babe ukukhetha okudumile kuzo zonke izimboni ezihlukahlukene. Phakathi kwalezi zingxubevange, i 5454 I-Aluminium Sheet Plate igqama ngamandla ayo aphezulu, ukumelana nokugqwala okuhle kakhulu, kanye nokwakheka okuphezulu. Lesi sihloko sicubungula imininingwane ye- 5454 I-Aluminium Sheet Plate, izinzuzo zayo, imininingwane, izakhiwo zemishini, izicelo, futhi nokuningi.
I 5454 I-Aluminium Sheet Plate iyingxubevange ye-aluminium-magnesium enamandla kakhulu esetshenziswa kabanzi embonini yokwakha imikhumbi nezokuthutha.. Idume ngokumelana nokugqwala okuhle kakhulu, ikakhulukazi emanzini olwandle nakwezinye izindawo ezigqwalile, okwenza kube ilungele izicelo zasolwandle.
Ukwakheka kwamakhemikhali we 5454 Ipuleti leshidi le-aluminium libalulekile kuzici zayo zokusebenza. Nansi incazelo enemininingwane:
| Ingxenye Yengxenye | Metric Percentage Range |
|---|---|
| I-Aluminium (Al) | 94.4 – 97.1 % |
| I-Chromium (Cr) | 0.05 – 0.20 % |
| Ithusi (Cu) | ≤ 0.10 % |
| Insimbi (Fe) | ≤ 0.40 % |
| Magnesium (Mg) | 2.4 – 3.0 % |
| IManganese (UMn) | 0.50 – 1.0 % |
| Okunye, ngamunye | ≤ 0.05 % |
| Okunye, inani | ≤ 0.15 % |
| I-silicon (Futhi) | ≤ 0.25 % |
| I-Titanium (Kwe) | ≤ 0.20 % |
| Zinc (Zn) | ≤ 0.25 % |
I 5454 Ipuleti leshidi le-aluminium linikeza uhla lwezinzuzo ezenza kube ukukhetha okukhethwa kukho ezinhlelweni eziningi:
I 5454 ipuleti aluminium sheet itholakala ukujiya ehlukahlukene, ububanzi, kanye nobude, futhi ingahlinzekwa ngezindlela ezahlukene:
| Ukucaciswa | Ibanga noma Izinketho |
| Ubukhulu | 0.2mm kuya ku-250 mm |
| Ububanzi | 500 mm kwe 2500 mm |
| Ubude | 1000 mm kwe 12000 mm |
| Ulaka | O, H111, H32, nabanye (H12 kuya ku-H38) |
| Ukwelashwa Okungaphezulu | Ukugaya, ukupholisha, ukuxubha, i-anodizing, njll. |
Ukuqonda izakhiwo zemishini ye 5454 Ipuleti le-aluminium leshidi libalulekile ekunqumeni ukufaneleka kwalo kwezinhlelo zokusebenza ezahlukahlukene, since the mechanical properties of 5454 alloys of different temperatures vary greatly, taking the O state as an example, the following table shows the mechanical properties of 5454-O:
| Impahla Mechanical | Metric Value | Conditions/Comments |
|---|---|---|
| Ukuqina, Brinell | 62 | AA; Okujwayelekile; 500 g load; 10 mm ibhola |
| Ukuqina, Knoop | 85 | Converted from Brinell Hardness Value |
| Ukuqina, Vickers | 72 | Converted from Brinell Hardness Value |
| Amandla Okuqina, Okokugcina | 248 I-MPa | AA; Okujwayelekile |
| 41.0 I-MPa | @ 371 °C / 700 °F | |
| 75.0 I-MPa | @ 316 °C / 601 °F | |
| 115 I-MPa | @ 260 °C / 500 °F | |
| 150 I-MPa | @ 204 °C / 399 °F | |
| 200 I-MPa | @ 149 °C / 300 °F | |
| 250 I-MPa | @ -28.0 °C / -18.4 °F | |
| 250 I-MPa | @ 24.0 °C / 75.2 °F | |
| 250 I-MPa | @ 100 °C / 212 °F | |
| 255 I-MPa | @ -80.0 °C / -112 °F | |
| 370 I-MPa | @ -196 °C / -321 °F | |
| Amandla Okuqina, Veza | 117 I-MPa | AA; Okujwayelekile |
| 29.0 I-MPa | @ 371 °C / 700 °F | |
| 50.0 I-MPa | @ 316 °C / 601 °F | |
| 75.0 I-MPa | @ 260 °C / 500 °F | |
| 105 I-MPa | @ 204 °C / 399 °F | |
| 110 I-MPa | @ 149 °C / 300 °F | |
| 115 I-MPa | @ -80.0 °C / -112 °F | |
| 115 I-MPa | @ -28.0 °C / -18.4 °F | |
| 115 I-MPa | @ 24.0 °C / 75.2 °F | |
| 115 I-MPa | @ 100 °C / 212 °F | |
| 130 I-MPa | @ -196 °C / -321 °F | |
| Elongation at Break | 25 % | @ 24.0 °C / 75.2 °F |
| 27 % | @ -28.0 °C / -18.4 °F | |
| 30 % | @ -80.0 °C / -112 °F | |
| 31 % | @ 100 °C / 212 °F | |
| 39 % | @ -196 °C / -321 °F | |
| 50 % | @ 149 °C / 300 °F | |
| 60 % | @ 204 °C / 399 °F | |
| 80 % | @ 260 °C / 500 °F | |
| 110 % | @ 316 °C / 601 °F | |
| 130 % | @ 371 °C / 700 °F | |
| 22 % | @ Thickness 1.59 mm / 0.0625 phakathi | |
| I-Modulus ye-Elasticity | 70.3 I-GPa | AA; Okujwayelekile; Isilinganiso sokucindezeleka nokucindezelwa. Compression modulus is about 2% greater than tensile modulus. |
| Notched Tensile Strength | 221 I-MPa | 2.5 cm width x 0.16 cm thick side-notched specimen, Kt = 17. |
| Ultimate Bearing Strength | 427 I-MPa | Edge distance/pin diameter = 2.0 |
| Bearing Yield Strength | 165 I-MPa | Edge distance/pin diameter = 2.0 |
| Isilinganiso sePisces | 0.33 | Estimated from trends in similar Al alloys. |
| Ukukhathala Amandla | 120 I-MPa | @ 5.00e+8 cycles; unnotched R. R. Moore rotating beam |
| Shear Modulus | 26.0 I-GPa | Estimated from similar Al alloys. |
| Amandla Shear | 159 I-MPa | AA; Okujwayelekile |
This table provides a comprehensive overview of the mechanical properties of the 5454 ingxubevange, including hardness, amandla aqinile, ubude, modulus of elasticity, futhi nokuningi, under various conditions and temperatures. I “Conditions/Comments” column provides additional details about the specific test parameters or the nature of the property measurement.
I 5454 Ipuleti leshidi le-aluminium lisetshenziswa ezinhlobonhlobo zezinhlelo zokusebenza ngenxa yenhlanganisela yalo eyingqayizivele yezakhiwo:
Ipuleti le-aluminium engu-5454-H32 lisetshenziselwa ukufakwa kwamathangi nezimoto zamathangi ezipholishiwe, enikeza ukuguquguquka kwezindawo ezonakalisayo:
| Impahla | Inani |
| Amandla Okuqina | 276 I-MPa |
| Isivuno Amandla | 207 I-MPa |
| I-Modulus ye-Elasticity | 70.3 I-GPa |
| Elongation at Break | 18%
@Temperature 24.0 °C |
| Ukuqina | 73 Brinell |
I 5454 I-H111 aluminium sheet sheet iphathwa ngokushisa ukuze ibe namandla aphezulu kanye ne-ductility ephansi, ifanele izakhiwo zasolwandle kanye nemikhumbi yokucindezela:
| Impahla | Inani |
| Amandla Okuqina | 262 I-MPa |
| Isivuno Amandla | 179 I-MPa |
| I-Modulus ye-Elasticity | 70.3 I-GPa |
| Elongation at Break | 14%
@Ubukhulu 1.59 mm |
| Ukuqina | 70 Brinell |
I 5454 O ipuleti le-aluminium sheet, esimweni sokuthunjwa, inikeza i-ductility ephezulu kanye nokuhleleka okuhle:
| Impahla | Inani |
| Amandla Okuqina | 165 I-MPa |
| Isivuno Amandla | 65 I-MPa |
| I-Modulus ye-Elasticity | 70 I-GPa |
| Elongation at Break | 25% |
| Ukuqina | 62 Brinell |
I 5454 I-aluminium ibonwa ngamazinga ahlukahlukene, okungase kube nomehluko omncane ezinqubweni zokukhiqiza noma ukubekezelelana:
Kubalulekile ukubonana nezinga elithile elidingekayo ukuze isicelo sakho siqinisekise ukuthi okokusebenza kuhlangabezana nezidingo ezidingekayo.
Ukuze uthole eminye imibuzo, imininingwane enemininingwane, noma ukufaka i-oda, thintana ne-Huasheng Aluminium, I-'5454 Aluminium Sheet Plate yakho ethembekile’ ifektri kanye nomthengisi. Ithimba lethu lochwepheshe likulungele ukukusiza ngazo zonke izidingo zakho ze-aluminium.
Isingeniso 1060 I-Aluminium ……
Isingeniso: E-Huasheng Al...
Isingeniso Ingxube ye-aluminium ……
Isingeniso 1070 I-Aluminium ……
Isingeniso ku 3004 I-Aluminium……
Isingeniso Siyakwamukela ku-Huas……
I-Henan Huasheng Aluminium Co., Ltd (HHALU ngamafuphi), isungulwe ku 2001, itholakala Huiguo Town, inhloko-dolobha edumile ye-Aluminium yesiFundazwe saseHenan, Ingumkhiqizi oqeqeshiwe futhi uhlanganyela ocwaningweni, ukuthuthukiswa, ukukhiqizwa, ukuthengisa kanye nenkonzo ye-aluminium sheet plate, ikhoyili ye-aluminium, i-aluminium foil, i-aluminium strip kanye nesiyingi se-aluminium.
Ngaphezu kwalokho, I-HHALU iphinde ithengise ipuleti le-aluminium yokwakha kanye nemikhumbi, ipuleti lesibuko se-aluminium, kanye ne-automotive aluminium alloy plate.
No.53, Umgwaqo we-Dongming, Zhengzhou, Henan, China
Copyright © Huasheng Aluminium 2023. Wonke Amalungelo Agodliwe.