| Sipesifikesonu | Ibiti o tabi Aw |
| Sisanra | 0.2mm to 250mm |
| Ìbú | 500 mm si 2500 mm |
| Gigun | 1000 mm si 12000 mm |
| Ibinu | O, H111, H32, ati awọn miiran (H12 si H38) |
| dada Itoju | Lilọ, didan, fẹlẹ, anodizing, ati be be lo. |
Aluminiomu alloys ti wa ni mo fun won versatility ati agbara-si-àdánù ratio, ṣiṣe wọn ni yiyan olokiki kọja awọn ile-iṣẹ lọpọlọpọ. Lara awọn alloys wọnyi, awọn 5454 Awo dì Aluminiomu duro jade fun agbara giga rẹ, o tayọ ipata resistance, ati ki o superior formability. Yi article delves sinu awọn pato ti awọn 5454 Awo dì Aluminiomu, awọn anfani rẹ, ni pato, darí-ini, awọn ohun elo, ati siwaju sii.
Awọn 5454 Awo Aluminiomu Aluminiomu jẹ ohun elo aluminiomu-magnesium alloy ti o ni agbara giga ti o lo pupọ ni awọn ile-iṣẹ ọkọ oju-omi ati awọn ile-iṣẹ gbigbe.. O jẹ olokiki fun resistance ipata ti o dara julọ, paapaa ni omi okun ati awọn agbegbe ibajẹ miiran, ṣiṣe awọn ti o apẹrẹ fun tona ohun elo.
Awọn kemikali tiwqn ti 5454 aluminiomu dì awo jẹ lominu ni si awọn oniwe-iṣẹ abuda. Eyi ni alaye didenukole:
| Eroja eroja | Metric Percentage Range |
|---|---|
| Aluminiomu (Al) | 94.4 – 97.1 % |
| Chromium (Kr) | 0.05 – 0.20 % |
| Ejò (Ku) | ≤ 0.10 % |
| Irin (Fe) | ≤ 0.40 % |
| Iṣuu magnẹsia (Mg) | 2.4 – 3.0 % |
| Manganese (Mn) | 0.50 – 1.0 % |
| Omiiran, kọọkan | ≤ 0.05 % |
| Omiiran, lapapọ | ≤ 0.15 % |
| Silikoni (Ati) | ≤ 0.25 % |
| Titanium (Ti) | ≤ 0.20 % |
| Zinc (Zn) | ≤ 0.25 % |
Awọn 5454 aluminiomu dì awo nfun kan ibiti o ti anfani ti o ṣe awọn ti o kan afihan wun fun ọpọlọpọ awọn ohun elo:
Awọn 5454 aluminiomu dì awo ti o wa ni orisirisi awọn sisanra, awọn iwọn, ati awọn ipari, ati pe a le pese ni oriṣiriṣi awọn ibinu:
| Sipesifikesonu | Ibiti o tabi Aw |
| Sisanra | 0.2mm to 250mm |
| Ìbú | 500 mm si 2500 mm |
| Gigun | 1000 mm si 12000 mm |
| Ibinu | O, H111, H32, ati awọn miiran (H12 si H38) |
| dada Itoju | Lilọ, didan, fẹlẹ, anodizing, ati be be lo. |
Agbọye awọn darí-ini ti awọn 5454 aluminiomu dì awo jẹ pataki fun a ti npinnu awọn oniwe-ìbójúmu fun orisirisi awọn ohun elo, since the mechanical properties of 5454 alloys of different temperatures vary greatly, taking the O state as an example, the following table shows the mechanical properties of 5454-O:
| Mechanical Ini | Metric Value | Conditions/Comments |
|---|---|---|
| Lile, Brinell | 62 | AA; Aṣoju; 500 g load; 10 mm rogodo |
| Lile, Knoop | 85 | Converted from Brinell Hardness Value |
| Lile, Vickers | 72 | Converted from Brinell Hardness Value |
| Agbara fifẹ, Gbẹhin | 248 MPa | AA; Aṣoju |
| 41.0 MPa | @ 371 °C / 700 °F | |
| 75.0 MPa | @ 316 °C / 601 °F | |
| 115 MPa | @ 260 °C / 500 °F | |
| 150 MPa | @ 204 °C / 399 °F | |
| 200 MPa | @ 149 °C / 300 °F | |
| 250 MPa | @ -28.0 °C / -18.4 °F | |
| 250 MPa | @ 24.0 °C / 75.2 °F | |
| 250 MPa | @ 100 °C / 212 °F | |
| 255 MPa | @ -80.0 °C / -112 °F | |
| 370 MPa | @ -196 °C / -321 °F | |
| Agbara fifẹ, So eso | 117 MPa | AA; Aṣoju |
| 29.0 MPa | @ 371 °C / 700 °F | |
| 50.0 MPa | @ 316 °C / 601 °F | |
| 75.0 MPa | @ 260 °C / 500 °F | |
| 105 MPa | @ 204 °C / 399 °F | |
| 110 MPa | @ 149 °C / 300 °F | |
| 115 MPa | @ -80.0 °C / -112 °F | |
| 115 MPa | @ -28.0 °C / -18.4 °F | |
| 115 MPa | @ 24.0 °C / 75.2 °F | |
| 115 MPa | @ 100 °C / 212 °F | |
| 130 MPa | @ -196 °C / -321 °F | |
| Elongation ni Bireki | 25 % | @ 24.0 °C / 75.2 °F |
| 27 % | @ -28.0 °C / -18.4 °F | |
| 30 % | @ -80.0 °C / -112 °F | |
| 31 % | @ 100 °C / 212 °F | |
| 39 % | @ -196 °C / -321 °F | |
| 50 % | @ 149 °C / 300 °F | |
| 60 % | @ 204 °C / 399 °F | |
| 80 % | @ 260 °C / 500 °F | |
| 110 % | @ 316 °C / 601 °F | |
| 130 % | @ 371 °C / 700 °F | |
| 22 % | @ Thickness 1.59 mm / 0.0625 ninu | |
| Modulu ti Elasticity | 70.3 GPA | AA; Aṣoju; Apapọ ẹdọfu ati funmorawon. Compression modulus is about 2% greater than tensile modulus. |
| Notched Tensile Strength | 221 MPa | 2.5 cm width x 0.16 cm thick side-notched specimen, Kt = 17. |
| Ultimate Bearing Strength | 427 MPa | Edge distance/pin diameter = 2.0 |
| Bearing Yield Strength | 165 MPa | Edge distance/pin diameter = 2.0 |
| Pisces ratio | 0.33 | Estimated from trends in similar Al alloys. |
| Agbara rirẹ | 120 MPa | @ 5.00e+8 cycles; unnotched R. R. Moore rotating beam |
| Modulu rirẹ | 26.0 GPA | Estimated from similar Al alloys. |
| Irẹrun Agbara | 159 MPa | AA; Aṣoju |
This table provides a comprehensive overview of the mechanical properties of the 5454 alloy, including hardness, agbara fifẹ, elongation, modulus of elasticity, ati siwaju sii, under various conditions and temperatures. Awọn “Conditions/Comments” column provides additional details about the specific test parameters or the nature of the property measurement.
Awọn 5454 aluminiomu awo awo ri lilo ni kan jakejado orun ti ohun elo nitori awọn oniwe-oto apapo ti-ini:
Awo awo aluminiomu 5454-H32 ni a lo fun awọn tanki idabobo ati awọn ọkọ ayọkẹlẹ ojò didan, n funni ni ibamu si awọn agbegbe ibajẹ:
| Ohun ini | Iye |
| Agbara fifẹ | 276 MPa |
| Agbara Ikore | 207 MPa |
| Modulu ti Elasticity | 70.3 GPA |
| Elongation ni Bireki | 18%
@Temperature 24.0 °C |
| Lile | 73 Brinell |
Awọn 5454 H111 aluminiomu awo awo ti wa ni ooru-mu fun agbara ti o ga ati kekere ductility, o dara fun awọn ẹya omi okun ati awọn ohun elo titẹ:
| Ohun ini | Iye |
| Agbara fifẹ | 262 MPa |
| Agbara Ikore | 179 MPa |
| Modulu ti Elasticity | 70.3 GPA |
| Elongation ni Bireki | 14%
@Sisanra 1.59 mm |
| Lile | 70 Brinell |
Awọn 5454 Eyin aluminiomu awo awo, ni annealed ipinle, nfun ga ductility ati ti o dara formability:
| Ohun ini | Iye |
| Agbara fifẹ | 165 MPa |
| Agbara Ikore | 65 MPa |
| Modulu ti Elasticity | 70 GPA |
| Elongation ni Bireki | 25% |
| Lile | 62 Brinell |
Awọn 5454 Aluminiomu ti wa ni mọ nipa orisirisi awọn ajohunše, eyi ti o le ni awọn iyatọ diẹ ninu awọn ilana iṣelọpọ tabi awọn ifarada:
O ṣe pataki lati kan si boṣewa kan pato ti o nilo fun ohun elo rẹ lati rii daju pe ohun elo pade awọn ibeere pataki.
Fun siwaju ìgbökõsí, alaye ni pato, tabi lati paṣẹ, olubasọrọ Huasheng Aluminiomu, rẹ gbẹkẹle '5454 Aluminiomu Sheet Plate’ factory ati alatapọ. Ẹgbẹ wa ti awọn akosemose ti šetan lati ṣe iranlọwọ fun ọ pẹlu gbogbo awọn aini aluminiomu rẹ.
Ọrọ Iṣaaju 1060 Aluminiomu ……
Ọrọ Iṣaaju: Huasheng Al…
Ifaara Aluminiomu alloy……
Ọrọ Iṣaaju 1070 Aluminiomu ……
Ifihan si 3004 Aluminiomu……
Ọrọ Iṣaaju Kaabọ si Huas……
Henan Huasheng Aluminum Co., Ltd., Ltd (HHALU fun kukuru), iṣeto ni 2001, wa ni Ilu Huiguo, awọn gbajumọ Aluminiomu olu ti Henan Province, O jẹ olupilẹṣẹ alamọdaju ati ṣe alabapin ninu iwadii naa, idagbasoke, gbóògì, tita ati iṣẹ ti aluminiomu dì awo, aluminiomu okun, aluminiomu bankanje, aluminiomu rinhoho ati aluminiomu Circle.
Ni afikun, HHALU tun ta awo aluminiomu fun ikole ati awọn ọkọ oju omi, aluminiomu digi awo, ati Oko aluminiomu alloy awo.
No.53, Ọna Dongming, Zhengzhou, Henan, China
Aṣẹ-lori-ara © Huasheng Aluminiomu 2023. Gbogbo awọn ẹtọ wa ni ipamọ.